Professional manufacturer for Fluoropolymer (PVDF) and Fluoroelastomer (FKM).  86-188-8877-8178,    export@flurine.com

Home > Products > FKM >

High Mooney Fluoroelastomer

High Mooney Fluoroelastomer

High Mooney Fluoroelastomer
CategoriesFKM
AlbumView larger image
BrandFlurine
Model26120 26140
FeaturesHigh Mooney viscosity
UsesGaskets, oil seals, diaphragm, sheets
FormsWhite or light-yellow flake
Update Time2019-11-21
Detail Information

Flurine® 26120 and 26140 are high Mooney Fluoroelastomer, which is comprised of vinylidene fluoride (VF2) and hexafluoropropylene (HFP), frequently used in many industries including automotive, fluid power, appliance and chemical industries. It has excellent mechanical strength, good demoulding properties and low compression set. It is resistant to oils, fuels, aliphatic series, aromatic hydrocarbons, lubricants, and most mineral acids.

General

Features

High Mooney viscosity

Uses

Gaskets, oil seals, diaphragm, sheets

Forms

White or light-yellow flake

Items

Typical Value

Test Method

26120

26140

Physical Properties

Fluorine Contentmass%

66

66

 

Densityg/cc

1.80~1.82

1.80~1.82

ASTM D297

Mooney Viscosity

110~129

130~160

ASTM D1646 ML 1+10 at 121°C

Water content

0.06

0.06

ASTM D 5668

Solubility

Soluble in lower ketones and esters

 

Vulcanization Properties

T10(s)

<80

<70

ASTM D5289

T90(s)

<150

<140

ASTM D5289

Mechanical Properties

Tensile strengthMPa

14.0

14.5

ASTM D412 Method A

100% Modulus

5.8

6.2

ASTM D412 Method A

Elongation at Break%

170

160

ASTM D412 Method A

Tearing Strength(KN/m)

21

22

ASTM D624

Hardness, Shore A

78

78

ASTM D2240, Type A

Compression Set

17

16

ASTM D395, Test B 70 hours at 200℃

Air-oven aging

ISO 188 After Dry Heat Aging;70 hours at 230℃

Tensile strength change rate%

+4

+2

ASTM D412 Method A

Elongation at Break change rate(%)

-3

-3

ASTM D412 Method A

Hardness change, Shore A

0

+1

ASTM D2240, Type A 

Thermal Properties

Glass Transition Temp, Tg(℃)

-20

-20

ASTM D1329

Brittleness Temperature(℃)

-30

-30

ASTM D2137

Chemical resistance Properties

Resistance to liquids

3 # standard oil

Volume change rate(%)

+1

+1

ASTM D471 72 hours at 150℃

Mass change rate(%)

+1

+1

ASTM D471 72 hours at 150℃

Formulation

Curing condition

Polymer            100      MT carbon black,N990   30

Calcium hydroxide    6        Magnesium oxide         3

Fluorocure-5#        2.5

Press

Oven

6min at 177°C

24h at 230°C


1)Store and use all fluoroelastomers only in a well-ventilated area.

2)Do not smoke in areas contaminated with dust from fluoroelastomers.

3)Avoid eye contact. After handling fluoroelastomers wash any skin that came in contact with the product with soap and water.

4)Potential hazards, including evolution of toxic vapors, exist during compounding or processing under high temperatures. 

5)Before processing the fluoroelastomers, read and consult the MSDS, and follow all label directions and operation cautions.

1)Fluoroelastomers be packed in PVC bags in the shape of rubber film, each bag weight 5KGS, and finally be put into a carton. Each carton contains 5 bags with net weight 25KGS.

2)It must be stored in a clean, cool, and dry place. The storage life is one year from the date of production. It must be re-inspected if over one year and only can use if qualified.

3)It is transported as non-dangerous chemicals. Avoid excessive vibration and far away from pollution, sunshine and water during the transport.
Please send your message to us
*Email
Tel
*Title
*Content

Agree to use terms of service

Categories
Contact Person
leave a message:
Contact Now
Address:
No.5, Weiyi Road, Shangyu Hangzhou Gulf Chemical Industrial Zone,          Zhejiang, China 312369
subscription
Mobile page