Zheflon® FL2006 PVDF- Extrusion Grade

Zheflon® FL2006 PVDF- Extrusion Grade
Zheflon® FL2006 PVDF- Extrusion GradeZheflon® FL2006 PVDF- Extrusion Grade

Zheflon® FL2006 PVDF- Extrusion Grade

FL2006 PVDF homopolymer is medium and low viscosity grade that with high purity, use for extruded pipe, bar, plates.
CategoriesPVDF for Lithium Batteries
BrandZheflon PVDF & Flurine FKM Manufacturer
ModelFL2006
FeaturesHomopolymer,Medium and low viscosity
UsesExtruded pipe, Bar, Plate
FormsTranslucent white particles
Processing technologySuspension PVDF
Update TimeMar 19,2024
Detail Information

Zheflon®FL2006 PVDF homopolymer is medium and low viscosity grade that with high purity. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of extrusion.

General

Features

HomopolymerMedium and low viscosity

Uses

Extruded pipe, Bar, Plate

Forms

Translucent white particles

Items

Typical Value FL2006

Test Method

Physical Properties

Density(g/cc)

1.77~1.79

ASTM D792

Melt Flow Rate(g/10min)

2.0~8.0

Load 5kg,230℃,ASTM D1238

Melt viscosity(Kps)

11~17

Shear Rate 100 1/s,ASTM D3835

 

Water Absorption(%)(Time 24 hr)

≤0.040

ISO 62

Linear Mold Shrinkage(cm/cm)

0.0200~0.0300

 

Molecular Properties

Molecular weight(Da)

300,000~390,000

GPC,DMF,ISO 16014

Intrinsic viscosity(dl/g)

1.00~1.20

30℃,DMAC

Molecular weight distribution

1.8-2.3

GPC,DMF,ISO 16014

Mechanical Properties

Tensile Modulus(Thickness2.00mm)(MPa)

1700~2500

1.0mm/min,ASTM D638

Flexural Modulus(Thickness2.00mm)(MPa)

1500~2300

2.0mm/min,ASTM D790

Yield Strength(Thickness2.00mm)(MPa)

50.0~57.0

50mm/min,ASTM D638

Break Strength(Thickness2.00mm)(MPa)

20.0~50.0

50mm/min,ASTM D638

Elongation at Yield(%)

5.0~10

50mm/min,ASTM D638

Elongation at Break(%)

20~50

50mm/min,ASTM D638

Hardness, Shore D(Thickness2.00mm)

75~80

ASTM D2240

Izod Impact, Notched(Thickness 4.00mm, 23℃)(J/m)

100~200

Notched V 10 mm

ASTM D256

Thermal Properties

Melting Point(℃)

169~173

ASTM D3418

Crystallization Temperature(DSC peak)(℃)

137~144

ASTM D3418

Glass Transition Temp, Tg(℃)

-32.0

ASTM E1356

Decomposition Temperature(℃)

375

1% wt. loss / in air

Vicat Softening Point(℃)

135~145

ASTM D1525

Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(℃)

102~110

After annealing 150℃,16h

ASTM D648

Electrical Properties

Surface Resistance(ohm)

≥1.00E+14

Voltage<1V,After 2 min—500V

ASTM D257

Electrical Resistivity(ohm·cm)

≥1.00E+14

Intensity=10mA,After 2 min@23℃

ASTM D257

Dielectric strength(Thickness 1.00mm,23℃)(KV/mm)

20~25

ASTM D149

Dielectric constant(1kHz,23℃)

7.0~10.0

ASTM D150

Burning Properties

UL Flame retardant grade(0.100mm)

V-0

UL94

Oxygen Index(3.00mm)

44%

ASTM D2683


1.PVDF should be processed under 260℃,to avoid producing toxic gases;

2.PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds;

3.Operators should take good care of personal protection during the use procedure and processing.


PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.

Contact Immediately

We have a dedicated team of technical experts ready to assist you with your most challenging projects. Discover cost-effective customized solutions for exceptional performance and value. Contact us today – we are eager to take on the challenge!
*Email
Name
Tel
*Title
*Content
Upload
  • Only supports .rar/.zip/.jpg/.png/.gif/.doc/.xls/.pdf, maximum 20MB.

Let's Innovate Together

We have a dedicated team of technical experts ready to help you with your most challenging projects, so contact us today - we're ready for the challenge!
Founded 2007, is a tech enterprise specializing in fluorine-based materials. We drive renewable energy and sustainability through innovation.