Zheflon® FL2305 Offshore Pipeline Grade PVDF

Zheflon® FL2305 Offshore Pipeline Grade PVDF

Zheflon® FL2305  Offshore Pipeline Grade PVDF
Zheflon® FL2305  Offshore Pipeline Grade PVDFZheflon® FL2305  Offshore Pipeline Grade PVDF
CategoriesPVDF for others
AlbumView larger image
BrandFlurine
Model2305
FeaturesCopolymer, medium melt viscosity
UsesOffshore pipeline
FormsTranslucent white particles
Update Time2019-09-18
Detail Information

Zheflon®FL2305 is a medium melt viscosity polyvinylidene fluoride copolymer,Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of injection.


General

Features

Copolymer, medium melt viscosity

Uses

Offshore pipeline

Forms

Translucent white particles

Items

Typical Value

Test Method

Density(g/cc)

1.75~1.80

ASTM D792

Melt Flow Rate(g/10min)

2.0~6.0

Load10kg,230℃,ASTM D1238

Water Absorption(%)(Time 24 hr)

≤0.040

ISO 62

Linear Mold Shrinkage(cm/cm)

0.0200~0.0300

 

Molecular Properties

 

 

Molecular weight(Da)

400,000~450,000

GPC,DMF,ISO 16014

Intrinsic viscosity(dl/g)

1.20~1.30

30℃,DMAC

Molecular weight distribution

1.8-2.3

GPC,DMF,ISO 16014

Mechanical Properties

 

 

Tensile Modulus(Thickness2.00mm)(MPa)

1200~1500

1.0mm/min,ASTM D638

Flexural Modulus(Thickness2.00mm)(MPa)

1000~1500

2.0mm/min,ASTM D790

Yield Strength(Thickness2.00mm)(MPa)

40.0~50.0

50mm/min,ASTM D638

Break Strength(Thickness2.00mm)(MPa)

30.0~40.0

50mm/min,ASTM D638

Elongation at Yield(%)

10.0~20

50mm/min,ASTM D638

Elongation at Break(%)

≥30

50mm/min,ASTM D638

Hardness, Shore D(Thickness2.00mm)

70~80

ASTM D2240

Thermal Properties

 

 

Melting Point(℃)

170~174

ASTM D3418

Crystallization Temperature(DSC peak)(℃)

142~146

ASTM D3418

Glass Transition Temp, Tg(℃)

-30.0

ASTM E1356

Vicat Softening Point(℃)

167

ASTM D1525

Decomposition Temperature(℃)

375

1% wt. loss / in air

Electrical Properties

 

 

Surface Resistance(ohm)

≥1.00E+14

Voltage<1V,After 2 min—500V

ASTM D257

Electrical Resistivity(ohm·cm)

≥1.00E+14

Intensity=10mA,After 2 min@23℃

ASTM D257

Dielectric strength(Thickness 1.00mm,23℃)(KV/mm)

20~25

ASTM D149

Dielectric constant(1kHz,23℃)

7.0~10.0

ASTM D150

Burning Properties

UL Flame retardant grade(0.100mm)

V-0

UL94

Oxygen Index(3.00mm)

44%

ASTM D2683


1.PVDF should be processed under 260℃,to avoid producing toxic gases;

2.PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds;

3.Operators should take good care of personal protection during the use procedure and processing.


PVDF is packed in PE plastic bag and then be put into a drum with the net weight 25KGS. It must be stored in clean, cool, dry place.

Please send your message to us
*Email
Tel
*Title
*Content

Agree to use terms of service

Categories
Contact Person
leave a message:
Contact Now
Address:
No.5, Weiyi Road, Shangyu Hangzhou Gulf Chemical Industrial Zone,          Zhejiang, China 312369
subscription
Mobile page